| About |
|---|
| Jackdaw PLA HS10VN6611是一种聚乳酸 (PLA)产品,。 它可以通过挤出进行加工,在欧洲有供货。 主要特性为:环保/绿色。&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3500 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 60.0 | MPa | ASTM D638 , ISO 527-2 |
| fracture | 48.0 | MPa | ISO 527-2 |
| — | 48.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.5 | % | ASTM D638 , ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 23.0 | kJ/m² | ASTM D256 |
| Charpy Unnotch Impact strength | 23 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 55.0 | ℃ | ASTM D648 |
| Melting peak temperature | 148 | ℃ | ASTM D2117 , ISO 1218 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |