| About |
|---|
| 11X02 is a HP-LLDPE blown film grade designed for easy processing applications which combines balanced film physical properties with good opticals. Features General purpose Easy processing Good opticals Applications Blown film grade&& |
| Product Description | |
|---|---|
| Supplier | Jam |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Smoothness,High anti-blocking,Inoxidizability |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.911 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | 15.0 to 180 | µm | |
| test | 25 | µm | |
| Secant modulus | |||
| 2% secant, MD: 25 µ m, blow molded film | 162 | MPa | |
| 2% secant, TD: 25 µ m, blow molded film | 188 | MPa | |
| tensile strength | |||
| MD, yield, 25 µ m, blow molded film | 10.5 | MPa | |
| TD, yield, 25 µ m, blow molded film | 9.50 | MPa | |
| MD, fracture, 25 µ m, blow molded film | 29.5 | MPa | |
| TD, fracture, 25 µ m, blow molded film | 25.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 25 µ m, blow molded film | 720 | % | |
| TD, fracture, 25 µ m, blow molded film | 770 | % | |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 120 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD: 25 µ m, blow molded film | 180 | g | |
| TD: 25 µ m, blow molded film | 400 | g |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 38 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 22 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow（up Ratio） | 2.00 to 3.00 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |