| About |
|---|
| 486H2 is a HDPE copolymer for blown film, general purposes. This grade is wall suited for film applications requiring a good pracessability, and outstanding mechanical properties. Features Grade under final development, to be industrialised. Applications Blown Film High Mechanicals&& |
| Product Description | |
|---|---|
| Supplier | Jam |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Inoxidizability,Copolymer |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.25 | g/10min | ASTM D1238 |
| Flow Rate Ratio | > 25.0 | ASTM D1238 | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 15 | µm | |
| Secant modulus | |||
| 2% secant, MD: 15 µ m, blow molded film | 700 | MPa | |
| 2% secant, TD: 15 µ m, blow molded film | 650 | MPa | |
| tensile strength | |||
| MD, fracture, 15 µ m, blow molded film | 32.0 | MPa | |
| TD, fracture, 15 µ m, blow molded film | 17.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 15 µ m, blow molded film | 500 | % | |
| TD, fracture, 15 µ m, blow molded film | > 700 | % | |
| Drop hammer impact | |||
| 15 µ m, blow molded film | 140 | g | ASTM D1709-A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Titanium | 3 | ppm |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |