| Jampilen H1022 is a natural polypropylene block copolymer with high melt viscosity and excellent low-temperature impact strength. It contains basic stabilization additives.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | High Viscosity,Block Copolymer,Good stability,low-temperature impact resistance |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.901 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30℃ | 3.0 | kJ/m² | |
| 0℃ | 7.0 | kJ/m² | |
| 23℃ | 35 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 75.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 149 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 165 | ℃ | ISO 3146 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 66 | ISO 868 | |
| Tensile modulus | 1100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 25.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2/50 |
| Tensile creep modulus | |||
| 1 hr | 1020 | MPa | ISO 899-1 |
| Flexural creep modulus | |||
| 1000 hr | 500 | MPa | ISO 6602 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |