| About |
|---|
| “Jampilen HP422H” is a modified homopolymer designed for the high speed production of BOPP films, wherein an outstanding extrusion stability, thickness variation control, a very high drawability and readiness to a two way orientation would be achieved. The product contains a reinforced processing stabilization and features low water carry-over properties. “Jampilen HP422H” does not contain any slip or antistatic agent and is Calcium Stearate free. The Product is particularly suitable for metalizing film.BOPP films produced with “Jampilen HP422H” feature goodmechanical properties, even at low temperatures, excellentbarrier against moisture, odors, oils and oxygen and goodtransparency and gloss.Monolayer or coextruded films made of “Jampilen HP422H” with a thickness ranging from 20 to 40 µm are used for the packaging of foodstuffs, cosmetics, CDs and DVDs. Features: High impact strength High puncture resistance Good transparency and gloss Homopolymer Typical Applications: Food packaging film Packaging of cosmetics, CDs and DVDs Barrier film&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good surface appearance,High impact resistance,Good dissection,Retention of aroma ,Quick molding cycle,Low odor,Moisture resistance,Electroplating,Grease resistance,Block resin,Puncture Resistant,Low water portability,Homopolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.1 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 92.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 154 | ℃ | ASTM D1525 2 |
| Accelerate oven aging | |||
| 150℃ | 500 | hr | ASTM D3012 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 20 µm | 0.50 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 | |
| tensile strength | |||
| yield | 35.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 12 | % | ASTM D638 |
| Bending modulus | 1550 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |