| About |
|---|
| “Jampilen HP515M” is a polypropulene homopolymer developed for the high speed extrusion of transparent cast and blown films. It is formulated with slip and antiblocking agents. “Jampilen HP515M” is suitable for the extrusion of low thickness films and can be used for films from 15 up to 150 um. In comparison with standard polypropylene types for film production, “Jampilen HP515M” allows for faster processing due to its peculiar structure and composition. Films made with “Jampilen HP515M” show a good behavior on winding rolls and in cutting section and feature very high transparency, high gloss and good printability after corona treatment. Features: Excellent processability High transparency and gloss Antiblock properties Homopolymer Typical Applications: Shopping bags Packaging for snacks, bakery products, books, blankets, hosiery and shirts Stationery folders Twines and ropes&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good surface appearance,Smoothness,Good Printability,High anti-blocking,Homopolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 92.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 150 | ℃ | ASTM D1525 2 |
| Accelerate oven aging | |||
| 150℃ | 360 | hr | ASTM D3012 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 86 | ASTM D2457 | |
| Haze | 1.2 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 95 | ASTM D785 | |
| tensile strength | |||
| yield | 32.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 12 | % | ASTM D638 |
| Bending modulus | 1300 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |