Jampilen HP648S

About
Jampilen HP648S is a high melt flow homopolymer with a narrow molecular weight distribution. Jampilen HP648S is designed for the high speed injection molding of thin-walled items with a good transparency and optimum antistatic properties. Due to its outstanding flow properties, its very high stiffness and excellent dimensional stability, this grade can be molded at very high speeds producing thin-walled parts, even with complicated shapes, without distortion. In many of applications Jampilen HP648S can replace traditional materials such as polystyrene since the product exhibits excellent processability, low residual stress, low shrinkage and warpage on top of the advantages typical of polypropylene such as light weight, low odour transfer, high chemical resistance and a good balance of mechanical properties.&&

About

Jampilen HP648S is a high melt flow homopolymer with a narrow molecular weight distribution. Jampilen HP648S is designed for the high speed injection molding of thin-walled items with a good transparency and optimum antistatic properties. Due to its outstanding flow properties, its very high stiffness and excellent dimensional stability, this grade can be molded at very high speeds producing thin-walled parts, even with complicated shapes, without distortion. In many of applications Jampilen HP648S can replace traditional materials such as polystyrene since the product exhibits excellent processability, low residual stress, low shrinkage and warpage on top of the advantages typical of polypropylene such as light weight, low odour transfer, high chemical resistance and a good balance of mechanical properties.&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Low warping,Good Clarity,Good Dimensional Stability,High liquidity,Low Residuals,Low contractility,Quick molding cycle,Low odor,Weight distribution,Solvent resistance,Antistatic property,Homopolymer
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D1505
Melt Flow Rate
230℃，2.16kg	35	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	29	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	110	℃	ASTM D648
Vicat Softening Temp	155	℃	ASTM D1525 1
Accelerate oven aging
150℃	360	hr	ASTM D3012

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	102		ASTM D785
tensile strength
yield	35.0	MPa	ASTM D638
Tensile strain
yield	10	%	ASTM D638
Bending modulus	1500	MPa	ASTM D790

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.