Jampilen RCXP599

About
Jampilen RCXP599 is a medium modified random copolymer for the production of cast and blown films with reduced blooming effect. Jampilen RCXP599 is formulated with slip and antiblocking agents. Jampilen RCXP599 offers easy processing on both cast and water-quenched blown film lines. The mechanical properties of films made with Jampilen RCXP599 are outstanding and the optical characteristics are superior to films made with conventional random copolymers. The seal initiation temperature is about 130°C and the blooming effect is minimal. Due to the good heat weldability, Jampilen 599 is suitable for monolayer films as well as sealing layers in coextruded films or laminated structures (e.g. with BOPP, PA, polyester or aluminum).&&

About

Jampilen RCXP599 is a medium modified random copolymer for the production of cast and blown films with reduced blooming effect. Jampilen RCXP599 is formulated with slip and antiblocking agents. Jampilen RCXP599 offers easy processing on both cast and water-quenched blown film lines. The mechanical properties of films made with Jampilen RCXP599 are outstanding and the optical characteristics are superior to films made with conventional random copolymers. The seal initiation temperature is about 130°C and the blooming effect is minimal. Due to the good heat weldability, Jampilen 599 is suitable for monolayer films as well as sealing layers in coextruded films or laminated structures (e.g. with BOPP, PA, polyester or aluminum).&&

Product Description
Generic	PP copolymer
Material Status	Commercial: Active
Features	Excellent Processability,Smoothness,Optical performance,High anti-blocking,Random copolymer,Welding
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D1505
Melt Flow Rate
230℃，2.16kg	9.0	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	50	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	82.0	℃	ASTM D648
Vicat Softening Temp	135	℃	ASTM D1525 1
Accelerate oven aging
150℃	360	hr	ASTM D3012

optical performance	Nominal value	Unit	Test method
gloss	85		ASTM D2457
Haze	1.8	%	ASTM D1003

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	92		ASTM D785
tensile strength
yield	28.0	MPa	ASTM D638
Tensile strain
yield	13	%	ASTM D638
Bending modulus	1000	MPa	ASTM D790

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.