| About |
|---|
| “Jampilen RP230C” is a natural polypropylene random copolymer for extrusion applications which contains an enhanced stabilization package. It is specially suitable for pipe and fttings having high impact resistance. Features: Random copolymer Typical Applications: Pipes and Fittings&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Negative |
| Features | High impact resistance,Random copolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.35 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 25.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 12 | % | ASTM D638 |
| Bending modulus | 800 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 500 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 80.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 135 | ℃ | ASTM D1525 3 |
| Melting temperature | |||
| DSC | 148 | ℃ | ISO 3146 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |