| About |
|---|
| JPPCABSI engineering resin is designed to offer a balance of properties between impact strength, heat resistance and processability. It offers better processability than polycarbonate while offering high impact strength at both room and low temperatures compared to ABS. With a deflection temperature under load (264 psi, unannealed) of 230°F, JPPCABSI also offers high heat resistance compared to ABS. JPPCABSI engineering resin has been used in automotive instrument panel and interior trim applications.&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 3.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.70 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.15 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃，3.2mm | 430 | J/m | ASTM D256 |
| -30℃，3.2mm | 530 | J/m | ASTM D256 |
| 23℃，3.2mm | 730 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -29℃，3.18 mm，Total Energy | 62.1 | J | ASTM D3763 |
| 23℃，3.18 mm，Total Energy | 56.5 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.2 mm | 110 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 121 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 7.4E-5 | 1/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 53.1 | MPa | ASTM D638 |
| fracture | 44.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 130 | % | ASTM D638 |
| Bending modulus | 2340 | MPa | ASTM D790 |
| bending strength | |||
| yield | 82.7 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 10 mil Notch Depth |
| 4. 11.1 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |