| About |
|---|
| JPPPO20. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolitic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings and impellers, valve components and others.&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Hydrolysis stability,Low or no water absorption,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 9.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 96 | J/m | ASTM D256 |
| 23℃ | 120 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 650 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 22.6 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 141 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 143 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 135 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 138 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 2.9E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 8.3E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | 90.0 | ℃ | UL 746 |
| Electrical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 2.86 | ASTM D150 | |
| 60 Hz | 2.86 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 8.0E-4 | ASTM D150 | |
| 60 Hz | 8.0E-4 | ASTM D150 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Extreme oxygen index | 26 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| Level L | 106 | ASTM D785 | |
| Tensile modulus | 6200 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 90.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.6 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 5800 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 160 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.050 in/min |
| 5. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |