| K-Resin® KR05 alone or in blends, can be extruded into sheet and thermoformed on conventional equipment at high output rates. The favorable economics of K-Resin® SBC, along with high productivity, have made possible tough clear disposable drinking cups, lids and other packaging applications. INEOS Styrolution has several grades of K-Resin® SBC tailored for your sheet extrusion needs. K-Resin® KR05 will process on most conventional equipment, allowing the molder to run a crystal clear bottle without expensive machine modifications, special molds, different screws, or dryers. K-Resin® SBC are blow molded in a broad range of sizes and shapes, from small pill bottles and medical drainage units, to very tall display bottles. They can also be injection blow molded into extremely high impact bottles with glass-like clarity. FEATURES Excellent Clarity Good Stiffness Good Formability Good Toughness High Surface Gloss APPLICATIONS Bottles Molded Boxes and Containers Medical Devices Portion Packages Blister Packaging&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Food contact compliance,Good Rigidity,HB,Good surface appearance,Copolymer |
| Availabilitys | Latin America,Europe,North America,Asia Pacific,Africa & Middle East |
| Process Methods | Film extrusion,Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 7.5 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 24hr | 0.090 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Dart impact equipped with measuring instruments | |||
| 23℃，3.18 mm | 40.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 62.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 85.0 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 162 | ASTM D523 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ASTM D2240 | |
| tensile strength | |||
| yield | 26.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 230 | % | ASTM D638 |
| Bending modulus | |||
| 3.18 mm | 1800 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.18 mm | 37.2 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 220 | °C | |
| Mold temperature | 30 | °C | |
| Melt Temperature | 218 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |