| Cross-linkable High Density Polyethylene Compound TA 1117 HD is for use in industrial applications. Crosslinked TA 1117 HD has a beneficial combination of high density and high gel content which result in excellent chemical, abrasion and heat resistance. The properties of TA 1117 HD make it a preferred choice for oil and gas, and other aggressive industrial applications. TA 1117 HD is suitable for continuous service exposed to hydrocarbons at operating temperatures of 200°F (93°C).&& |
| Product Description | |
|---|---|
| Generic | XLPE |
| Material Status | Commercial: Active |
| Features | Crosslinked,High Heat Resistance,Copolymer,Good wear resistance,High density,Solvent resistance |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.947 | g/cm³ | ASTM D792 |
| Apparent density | 0.54 | g/cm³ | ASTM D1895 , ISO 60 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 1.0 | g/10min | ASTM D1238 |
| water content | < 0.020 | % | |
| Gel content | 75 | % | ASTM D2765 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 22.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 250 | % | ASTM D638 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| volatility | < 0.10 | % |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 154 to 177 | °C | |
| Barrel 2 zone temperature | 165 to 188 | °C | |
| Barrel 3 zone temperature | 177 to 200 | °C | |
| Barrel 4 zone temperature | 188 to 200 | °C | |
| Head temperature | 200 to 210 | °C | |
| Nozzle temperature | 190 to 215 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Karl Fischer titration (SIL 4.4) |
| 3. SIL 4.3 |
| 4. Control of the screw temperature may improve processing results. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |