| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | HPPA |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Low warping,Good surface appearance,High impact resistance,Quick molding cycle,Electroplating |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Shrinkage rate | Internal Method | ||
| TD | 0.67 | % | Internal Method |
| MD | 0.070 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.14 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 23000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 250 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.4 | % | ISO 527-2 |
| Bending modulus | 20400 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 370 | MPa | ISO 178 |
| Bending strain | |||
| fracture | 3.4 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 12 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | 80 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 223 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 209 | ℃ | ISO 75-2/A |
| Glass transition temperature | 55 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 4.0 to 12 | hr | |
| Recommended maximum moisture content | 0.090 | % | |
| Temperature at the rear of the barrel | 265-300 | °C | |
| Front temperature of material barrel | 280-330 | °C | |
| Processing (melt) temperature | 280-330 | °C | |
| Mold temperature | 50-130 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |