| About |
|---|
| Kalix® 2930 HFFR is a bio-sourced polyamide-based material specifically formulated to meet UL 94V2 @ 0.4 mm requirements for electronic devices. The material uses an advanced halogen-free flame retardant package expressly designed to minimize blooming, plate out, and other process related issues commonly associated with flame retardant materials. Black: Kalix® 2930 HFFR BK 000&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | HPPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good surface appearance,High impact resistance,Good Dimensional Stability,High liquidity,Sprayable,Quick molding cycle,Flame Characteristics,Electroplating,V-2 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | ||
| Shrinkage rate | Internal Method | ||
| TD | 0.70 | % | Internal Method |
| MD | 0.20 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.17 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10600 | MPa | ISO 527-2 |
| tensile strength | 130 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.4 | % | ISO 527-2 |
| Bending modulus | 10000 | MPa | ISO 178 |
| bending strength | 200 | MPa | ISO 178 |
| Fracture bending strain | 2.6 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 9.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | 55 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 65.0 | ℃ | DMA |
| Melting temperature | 223 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 12 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Barrel rear temperature | 265 to 275 | °C | |
| Barrel front temperature | 280 to 295 | °C | |
| Processing (melt) temperature | 260 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |