| Kalix® 2955 is a bio-sourced, polyamide-based compound with 55% by weight glass fiber reinforcement. This material is specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry. Black: Kalix® 2955 BK 000 White: Kalix® 2955 WH 000&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | HPPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good surface appearance,High impact resistance,Good Dimensional Stability,High liquidity,Sprayable,Quick molding cycle,Electroplating,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | ||
| Shrinkage rate | Internal Method | ||
| TD | 0.30 | % | Internal Method |
| MD | 0.090 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.090 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17800 | MPa | ISO 527-2 |
| tensile strength | 222 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2 |
| Bending modulus | 15800 | MPa | ISO 178 |
| bending strength | 330 | MPa | ISO 178 |
| Fracture bending strain | 3.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 22 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 100 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 20 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | 90 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 222 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 214 | ℃ | ISO 75-2/A |
| Glass transition temperature | 55.0 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 2.40 GHz | 4.13 | ASTM D2520 | |
| Dissipation factor | |||
| 2.4 GHz | 0.011 | ASTM D2520 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| >0.60 mm, black, white | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 12 | hr | |
| Recommended maximum moisture content | 0.090 | % | |
| Barrel rear temperature | 265 to 300 | °C | |
| Barrel middle temperature | 280 to 330 | °C | |
| Barrel front temperature | 280 to 330 | °C | |
| Processing (melt) temperature | 280 to 330 | °C | |
| Mold temperature | 50 to 130 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information. |
| 3. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |