| About |
|---|
| Kalix® 5950 HFFR is a halogen-free, flame retardant (UL-94 V0 at 0.4 mm), highly reinforced polyamide material specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry. Black: Kalix® 5950 BK 000 HFFR White: Kalix® 5950 WH 000 HFFR&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | HPPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good surface appearance,High impact resistance,Good Dimensional Stability,High liquidity,Sprayable,Halogen free,Flame Characteristics,Electroplating,Low moisture absorption,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.68 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD | 0.18 | % | Internal Method |
| MD | 0.060 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.11 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 20000 | MPa | ISO 527-2 |
| 50% RH，平衡 | 19700 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.8 | % | ISO 527-2 |
| Bending modulus | 19000 | MPa | ISO 178 |
| bending strength | 350 | MPa | ISO 178 |
| Fracture bending strain | 2.2 | % | ISO 178 |
| tensile strength | |||
| yield | 245 | MPa | ISO 527-2 |
| 50% RH, balanced | 183 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, balanced, 50% RH | 1.7 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 15 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | 50 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 255 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 247 | ℃ | ISO 75-2/A |
| Glass transition temperature | 40.0 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 2.40 GHz | 4.48 | ASTM D2520 | |
| Dissipation factor | |||
| 2.4 GHz | 0.011 | ASTM D2520 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm, all colors | V-0 | UL 94 | |
| 1.50 mm, all colors | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 12 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Barrel rear temperature | 270 | °C | |
| Barrel front temperature | 285 | °C | |
| Processing (melt) temperature | 275 to 285 | °C | |
| Mold temperature | 115 to 130 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information. |
| 3. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |