| About |
|---|
| POLYCARBONATES HIGH VISCOSITY TU 2226-173-00203335-2007, rev. 1-9 Production method: polycondensation in diphenylcarbonate and bisphenol-A melt. Application: production ofgoods through extrusion and injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Joint |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High Viscosity |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 5.5 to 7.5 | g/10min | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | > 60.0 | MPa | |
| Tensile strain | |||
| fracture | > 120 | % | |
| Bending modulus | > 2250 | MPa | |
| bending strength | > 90.0 | MPa | |
| compressive strength | > 76.0 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | > 75 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | > 150 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | > 89.0 | % | |
| Haze | < 0.80 | % | |
| Transparency and Brightness Index | > 90.0 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Impurities | 5.00 | pcs |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |