| Kepamid 1525SM3 is mineral filler 25% reinforced and impact modified polyamide-6. Good thermal property and impact strength with low warpage. It is applicable to automotive, electrical, electronic, and industrial parts.&& |
| Product Description | |
|---|---|
| Supplier | Korea Engineering |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low warping,High impact resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 235℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 220 | ℃ | DSC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 114 | ASTM D785 | |
| tensile strength | |||
| Yield, 23 ℃ | 61.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 25 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 3140 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 98.1 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Hopper temperature | 230 to 250 | °C | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 230 to 250 | °C | |
| Barrel front temperature | 230 to 250 | °C | |
| Nozzle temperature | 230 to 250 | °C | |
| Mold temperature | 40.0 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |