| About |
|---|
| Kepital® F10-01 A high-viscosity grade for extrusion of round bars, sheets and tubes Suitable for extrusion molding of thick-walled, void-free, and sink mark-reduced parts&&Kepital® F10-01 High viscosity grade, designed for stock shapes of extrusion. F10-01 is also good for injection molding of thick-walled where void and sink is concerned.&& |
| Product Description | |
|---|---|
| Supplier | Korea Engineering |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | High Viscosity,Copolymer,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.0 mm | 2.2 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2500 | MPa | ISO 527-2 |
| tensile strength | 63.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 40 | % | ISO 527-2 |
| yield | 10 | % | ISO 527-2 |
| Bending modulus | 2350 | MPa | ISO 178 |
| bending strength | 82.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 96.0 | ℃ | ISO 75-2/A |
| Melting temperature | 165 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.2E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 19 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 170 to 180 | °C | |
| Barrel middle temperature | 180 to 190 | °C | |
| Barrel front temperature | 190 to 200 | °C | |
| Nozzle temperature | 180 to 210 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | < 2.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |