| About |
|---|
| A medium-viscosity grade for general injection molding Features improved resistance in hot water and high temperature/humidity&& |
| Product Description | |
|---|---|
| Supplier | Korea Engineering |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Moisture resistance,Copolymer,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | 9.0 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | |||
| MD：3.0 mm | 2.0 | % | ASTM D955 |
| 3.0 mm | 2.0 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 60% RH | 0.22 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.5 | kJ/m² | ISO 179-1eA |
| Impact strength of cantilever beam notch | |||
| 3.2mm | 64 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 158 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 110 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Melting temperature | 165 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：20~80℃ | 1.3E-4 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | ASTM D257，IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257，IEC 60093 |
| Dielectric strength | 19 | kV/mm | ASTM D149，IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 3.70 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 7.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 80 | ASTM D785 | |
| tensile strength | |||
| Yield, 23 ℃ | 61.0 | MPa | ASTM D638 |
| Yield, 23 ℃ | 65.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 60 | % | ASTM D638 |
| Nominal tensile fracture strain | |||
| 23℃ | 35 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2600 | MPa | ASTM D790 |
| 23℃ | 2550 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 90.0 | MPa | ASTM D790 |
| 23℃ | 87.0 | MPa | ISO 178 |
| shear strength | |||
| 2.00 mm | 55.0 | MPa | ASTM D732 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |