| Kepital® FL2010 A medium-high viscosity grade for general injection molding. It was modified with 10% PTFE powder, and so suitable for parts requiring low wear and friction.&&Kepital® FL2010 10% PTFE powder filled grade, good for general injection molding. FL2010 is suitable for parts that are required of low wear and friction.&& |
| Product Description | |
|---|---|
| Supplier | Korea Engineering |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Lubricating,Good wear resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 8.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.0 mm | 2.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 55.0 | MPa | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | 14 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2400 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 80.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179-1eA |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 16 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |