| KetaSpire® KT-850P is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses. KetaSpire® KT-850P can be easily processed using typical injection molding and extrusion processes. The resin is also available as KetaSpire® KT-850 NT in a natural-color pellet form.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 10 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3650 | MPa | ASTM D638 |
| tensile strength | 96.5 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 5.2 | % | ASTM D638 |
| fracture | 20 to 30 | % | ASTM D638 |
| Bending modulus | 3860 | MPa | ASTM D790 |
| bending strength | 152 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 69 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 162 | ℃ | ASTM D648 |
| Glass transition temperature | 150 | ℃ | ASTM D3417 |
| Melting temperature | 340 | ℃ | ASTM D3417 |
| Linear coefficient of thermal expansion | |||
| MD：-50~50℃ | 4.3E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 354 | °C | |
| Barrel middle temperature | 366 | °C | |
| Barrel front temperature | 371 | °C | |
| Nozzle temperature | 374 | °C | |
| Mold temperature | 177 to 204 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |