| Description General Purpose, Medium Modulus Application Antenna Cover, Injection Parts for Lesuire & Sports&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 25 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD: 3.2 mm, injection molded | 0.60 to 1.0 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.60 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 23 ℃ | 95 | ASTM D2240 | |
| Shore D, 23 ℃, injection molding | 42 | ASTM D2240 | |
| tensile strength | |||
| Fracture, 2 mm | 29.4 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 2 mm | 800 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 78.5 | MPa | ASTM D790 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| 23℃ | 104 | kN/m | ASTM D624 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃，6.4mm | No Break | ASTM D256 | |
| 23℃，6.4mm | No Break | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm, injection molded | 65.0 | ℃ | ASTM D648 |
| Melting peak temperature | 180 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 26 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 190 to 210 | °C | |
| Barrel front temperature | 200 to 220 | °C | |
| Nozzle temperature | 200 to 220 | °C | |
| Processing (melt) temperature | 180 to 220 | °C | |
| Mold temperature | 10 to 35 | °C | |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel 1 zone temperature | 180 to 200 | °C | |
| Barrel 2 zone temperature | 190 to 210 | °C | |
| Barrel 3 zone temperature | 200 to 220 | °C | |
| Barrel 4 zone temperature | 200 to 220 | °C | |
| Connector temperature | 200 to 220 | °C | |
| Melt temperature | 180 to 220 | °C | |
| Nozzle temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |