| About |
|---|
| Description General Purpose, High Modulus Application Cable & Wire Jackets, Hose & Tubing, Sheet, etc.&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD: 3.2 mm, injection molded | 1.1 to 1.5 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃, injection molding | 57 | ASTM D2240 | |
| tensile strength | |||
| Fracture, 23 ℃, 2 mm, injection molding | 37.3 | MPa | ASTM D638 |
| Yield, 23 ℃, 2 mm, injection molding | 16.7 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 2 mm, injection molding | 700 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, 6.40 mm, injection molding | 216 | MPa | ASTM D790 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| 23℃ | 160 | kN/m | ASTM D624 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40 ℃, 6.4mm, injection molding | 98 | J/m | ASTM D256 |
| 23 ℃, 6.4mm, injection molding | No Break | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm, injection molded | 110 | ℃ | ASTM D648 |
| Melting peak temperature | 208 | ℃ | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 26 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 220 to 240 | °C | |
| Barrel front temperature | 225 to 245 | °C | |
| Nozzle temperature | 225 to 245 | °C | |
| Processing (melt) temperature | 210 to 240 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel 1 zone temperature | 210 to 230 | °C | |
| Barrel 2 zone temperature | 215 to 235 | °C | |
| Barrel 3 zone temperature | 225 to 245 | °C | |
| Barrel 4 zone temperature | 225 to 245 | °C | |
| Connector temperature | 225 to 245 | °C | |
| Melt temperature | 210 to 240 | °C | |
| Nozzle temperature | 215 to 255 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |