| About |
|---|
| KF 1000 PVDF homopolymer is a medium viscosity PVDF resin typically processed by extrusion This material offers excellent chemical resistance at ambient and elevated temperatures. PVDF is also inherently UV stable, mechanically tough, abrasion&& |
| Product Description | |
|---|---|
| Supplier | Kureha |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low Viscosity,Homopolymer,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 2.70 | kJ/m² | ASTM D256 |
| -20℃ | 3.00 | kJ/m² | ASTM D256 |
| 0℃ | 9.70 | kJ/m² | ASTM D256 |
| 20℃ | 15.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -31.0 | ℃ | ASTM D746 |
| Glass transition temperature | -35.0 | ℃ | DMA |
| Vicat Softening Temp | |||
| A50 | 172 | ℃ | ISO 306/A50 |
| Melting peak temperature | 173 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 140 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 1.6E-4 | 1/℃ | ISO 11359-2 |
| specific heat | |||
| 23℃ | 1200 | J/kg/℃ | JIS K7123 |
| Thermal conductivity coefficient | |||
| 23℃ | 0.17 | W/m/K | ASTM E1530 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+14 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 0.034 mm | 300 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 10.0 | ASTM D150 | |
| Dissipation factor | |||
| 1 kHz | 0.015 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | 44 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.420 | ASTM D542 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 78 | ISO 868 | |
| Tensile modulus | 2330 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 57.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 28 | % | ISO 527-2 |
| Bending modulus | 1570 | MPa | ISO 178 |
| bending strength | 74.0 | MPa | ISO 178 |
| Compression modulus | 1570 | MPa | ISO 604 |
| compressive strength | 74.0 | MPa | ISO 604 |
| Taber abraser | |||
| 1000 cycles, 1000 g | 31.0 | mg | ISO 9352 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，5.0kg | 6.0 to 9.0 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| balance | 0.030 | % | ASTM D570 |
| Solution viscosity | |||
| DMF，30℃ | 100 | cm³/g | |
| Apparent viscosity of melt | |||
| 240℃，50.0 sec^-1 | 2200 | Pa·s | ASTM D3835 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50N |
| 3. Type-IV |
| 4. 25°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |