| About |
|---|
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| 50mm/min | 47 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture 50mm/min | 8 | % | ISO 527-2 |
| bending strength | |||
| 2mm/min | 76 | MPa | ISO 178 |
| Bending modulus | |||
| 2mm/min | 2500 | MPa | ISO 178 |
| Rockwell hardness | 108 | R Scale | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 20 | KJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Load deformation temperature | |||
| 0.45MPa | 85 | ℃ | ISO 75-2 |
| 1.8MPa | 77 | ℃ | ISO 75-2 |
| Vicat Softening Temp | |||
| 1kg, 120℃/h | 96 | ℃ | ISO 306 |
| 5kg, 50℃/h | 86 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| 23℃ | 1.05 | g/cm³ | ISO 1183-1 |
| Melt Flow Rate | |||
| 200℃, 5kg | 2.0 | g/10min | ISO 1133-1 |
| 220℃, 10kg | 20 | g/10min | ISO 1133-1 |
| Moulding shrinkage | |||
| 23℃ | 0.4-0.7 | % | ISO 2577 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Melt Temperature | 215 | ℃ | |
| Barrel temperature | |||
| Posterior segment | 190 | ℃ | |
| Middle section | 200 | ℃ | |
| Front section | 210 | ℃ | |
| Mold temperature | 50 | ℃ | |
| Upper limit of processing temperature | 250 | ℃ | |
| Injection molding speed | 低速to中速 | ||
| Back pressure | 0-1000 | KPa | |
| Pre drying | 80-90, 2-4hr | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |