| About |
|---|
| KIBILAC® PW-997S is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant&& |
| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 3.80 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 21 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179 | |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 390 | J/m | ASTM D256 |
| 23℃，6.4mm | 250 | J/m | ASTM D256 |
| — | 20 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | 无断裂 | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 86.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed, 6.35 mm | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 96.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 105 | ℃ | ASTM D1525，ISO 306 |
| — | 108 | ℃ | ISO 306/A120 |
| B50 | 92.0 | ℃ | ISO 306 |
| B120 | 95.0 | ℃ | ISO 306/B120 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 93 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 88.0 | MPa | ISO 2039-1 |
| tensile strength | |||
| yield | 48.0 | MPa | ISO 527-2/50 |
| fracture | 42.0 | MPa | ISO 527-2/50 |
| 3.18 mm | 44.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 80 | % | ISO 527-2/50 |
| Bending modulus | 1800 | MPa | ISO 178 |
| bending strength | |||
| 6.35 mm | 64.7 | MPa | ASTM D790 |
| — | 65.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| drying temperature | 80.0 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Temperature of material cylinder zone 1 | 200 to 220 | °C | |
| Temperature of material cylinder zone 3 | 220 to 250 | °C | |
| Temperature of material cylinder zone 5 | 230 to 260 | °C | |
| Mouth temperature | 210 to 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 0.24 in/min |
| 4. 0.11 in/min |
| 5. 0.079 in/min |
| 6. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |