| Kingfa API-CG318是一种聚丙烯材料,含有的填充物为玻璃纤维增强材料。 该产品在亚太地区有供货,加工方式为:注射成型。 Kingfa API-CG318的主要特性有: 阻燃/额定火焰 良好的尺寸稳定性 美观 耐热 典型应用领域包括: 汽车行业 工程/工业配件&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good Dimensional Stability,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.90 | % | Internal Method |
| Shrinkage rate | 0.30 | % | Internal Method |
| ash content | 30 | % | ISO 3451-1 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0-5.0 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 140 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 108 | R 级 | ISO 2039-2 |
| tensile strength | |||
| 23℃ | 65.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.2 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 95.0 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 4500 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |