| About |
|---|
| Kingfa FRABS-518 AC是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa FRABS-518 AC的主要特性有: 阻燃/额定火焰 Flame Retardant 耐冲击 典型应用领域包括: 电气/电子应用 工具 |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Flame Characteristics,low-temperature impact resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.0 | g/10min | |
| 220℃，10.0kg | 35 | g/10min | |
| Shrinkage rate | |||
| 23℃ | 0.40 to 0.60 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 27 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 4.0 mm | 83.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed, 4.0 mm | 74.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 93.0 | ℃ | ISO 306/A120 |
| B50 | 84.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 101 | ISO 2039-2 | |
| tensile strength | 38.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 15 | % | ISO 527-2/50 |
| Bending modulus | 2100 | MPa | ISO 178 |
| bending strength | 60.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 155 to 175 | °C | |
| Barrel middle temperature | 165 to 185 | °C | |
| Barrel front temperature | 175 to 205 | °C | |
| Processing (melt) temperature | 165 to 205 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 0.00 to 1.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |