| Kingfa FRABS-V0是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:挤出或注射成型。 Kingfa FRABS-V0的主要特性有: 阻燃/额定火焰 High Toughness Kingfa FRABS-V0的典型应用领域为:电气/电子应用&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Ultra high toughness,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 200℃，5.0kg | 1.2 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃，3.2mm | 180 | J/m | ASTM D256 |
| 23℃，6.4mm | 140 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 80.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 102 | ℃ | ASTM D1525 3 |
| — | 93.0 | ℃ | ASTM D1525 4 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 22 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| tensile strength | 40.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 15 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ASTM D790 |
| bending strength | 58.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 180 to 210 | °C | |
| Barrel middle temperature | 190 to 220 | °C | |
| Barrel front temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |