| About |
|---|
| Kingfa FRHIPS-8002U是一种高抗冲聚苯乙烯材料,。 该产品在北美洲或亚太地区有供货,。 Kingfa FRHIPS-8002U的主要特性有: 阻燃/额定火焰 Flame Retardant 耐冲击 典型应用领域包括: 房屋 汽车行业&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | High impact resistance,Flame Characteristics,Low density,V-2 |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 90 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 77.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 96.0 | ℃ | ASTM D1525 4 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 99 | ASTM D785 | |
| tensile strength | |||
| 23 ℃, injection molding | 27.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, injection molding | 45 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, injection molding | 2250 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, injection molding | 40.0 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |