| About |
|---|
| Kingfa GFPP-10 is a Polypropylene material filled with 10% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa GFPP-10 are: Flame Rated Chemically Coupled Good Aesthetics Good Dimensional Stability Heat Resistant Typical applications include: Appliances Engineering/Industrial Parts&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Heat Resistance, Good,HB |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：23℃ | 0.60 to 1.2 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 70 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm, injection molded | 150 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm, injection molded | 135 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| tensile strength | |||
| 23 ℃, injection molding | 55.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, injection molding | 5.0 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, injection molding | 2500 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, injection molding | 70.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |