| Kingfa GFPP-L40是一种聚丙烯材料,含有的填充物为40% 长玻璃纤维。 该产品在亚太地区有供货,加工方式为:注射成型。 Kingfa GFPP-L40的主要特性有: 阻燃/额定火焰 抗翘曲 美观 耐热 良好的尺寸稳定性 典型应用领域包括: 家庭应用 工程/工业配件 汽车行业 电气用具&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance,Good Dimensional Stability,High Heat Resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Spiral flow length | 60.0 | cm | |
| Shrinkage rate | Internal Method | ||
| TD | 0.20 | % | |
| MD | 0.10 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 162 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 157 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Fiberglass length | 1.00 to 1.20 | cm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 112 | ISO 2039-2 | |
| tensile strength | |||
| fracture | 118 | MPa | ISO 527-2/10 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2/10 |
| Bending modulus | 7400 | MPa | ISO 178 |
| bending strength | 168 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 90.0 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 240 to 260 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Processing (melt) temperature | 230 to 250 | °C | |
| Mold temperature | 30.0 to 60.0 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |