| About |
|---|
| Kingfa JH-R2G15 is a Polycarbonate + ABS (PC+ABS) material filled with 15% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa JH-R2G15 are: Flame Rated Good Aesthetics Good Dimensional Stability Heat Resistant High Stiffness Typical applications include: Electrical/Electronic Applications Business/Office Goods Engineering/Industrial Parts Housings&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Good surface appearance,Good Dimensional Stability,High Heat Resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.30 to 0.50 | % | ISO 2577 |
| Ash Content | |||
| 825℃，40 min | 15 | % | ISO 3451-1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 80.0 | MPa | ISO 527-2/10 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2/10 |
| Bending modulus | 4500 | MPa | ISO 178 |
| bending strength | 125 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.0 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 50 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 4.0 mm | 120 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.6 mm in oil | 28 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 230 to 260 | °C | |
| Barrel middle temperature | 240 to 290 | °C | |
| Barrel front temperature | 250 to 300 | °C | |
| Processing (melt) temperature | 230 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 慢to中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |