| About |
|---|
| Kingfa JH950-402 is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa JH950-402 are: Flame Rated Flame Retardant Heat Resistant Typical applications include: Electrical/Electronic Applications Engineering/Industrial Parts&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Antifreeze,Good bond,Good wear resistance,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：23℃ | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 250 | J/m | ASTM D256 |
| 23℃，3.2mm | 340 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 120 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 105 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 28 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-0 | UL 94 | |
| Igniting temperature of the hot wire | |||
| 1.6 mm | 850 | ℃ | IEC 60695-2-13 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 114 | ASTM D785 | |
| tensile strength | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 30 | % | ASTM D638 |
| Bending modulus | 2300 | MPa | ASTM D790 |
| bending strength | 85.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 220 to 230 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Processing (melt) temperature | 220 to 240 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Back pressure | 0.00 to 1.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 2.0 in/min |
| 4. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |