| About |
|---|
| Kingfa JH960 6300是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,。 该产品在亚太地区或北美洲有供货,加工方式为:注射成型。 Kingfa JH960 6300的主要特性有: 阻燃/额定火焰 Flame Retardant 无卤素 耐化学品 耐热 典型应用领域包括: 电气/电子应用 印刷应用 工具&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High liquidity,Hydrolysis stability,Sprayable,Halogen free,Flame Characteristics,High Heat Resistance,Electroplating,Solvent resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 19 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -10℃，3.2mm | 380 | J/m | |
| 23℃，3.2mm | 470 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 100 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 88.0 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 19 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 5VB | ||
| 3.20 mm | V-0 5VA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| tensile strength | 55.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| Bending modulus | 2600 | MPa | ASTM D790 |
| bending strength | 85.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 85.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 220 to 250 | °C | |
| Barrel middle temperature | 230 to 255 | °C | |
| Barrel front temperature | 235 to 265 | °C | |
| Processing (melt) temperature | 230 to 250 | °C | |
| Mold temperature | 40.0 to 80.0 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |