| About |
|---|
| Kingfa LDP-3008 is a Polypropylene material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa LDP-3008 are: Flame Rated Flame Retardant High Gloss Typical application of Kingfa LDP-3008: Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Low to No Fogging,Flame Characteristics |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 4.0 mm | 105 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 115 | ℃ | ISO 306/A120 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| 3.00 mm, solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 0.8 mm | 875 | ℃ | |
| 1.6 mm | 800 | ℃ | |
| 3.2 mm | 725 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 80 | ISO 2039-2 | |
| tensile strength | 25.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 30 | % | ISO 527-2/50 |
| Bending modulus | 1500 | MPa | ISO 178 |
| bending strength | 38.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 190 to 210 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 0.350 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |