| About |
|---|
| Kingfa LONOY-6100 is a Polycarbonate + PBT (PC+PBT) material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa LONOY-6100 are: Flame Rated RoHS Compliant Flame Retardant Good Processability Chemical Resistant Typical applications include: Electrical/Electronic Applications Engineering/Industrial Parts Housings Outdoor Applications&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Flame Characteristics,Solvent resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 30 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 0.70 to 1.2 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 54.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 60 | % | ASTM D638 |
| Bending modulus | 2000 | MPa | ASTM D790 |
| bending strength | 80.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 600 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 112 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 101 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 30 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 230 to 245 | °C | |
| Barrel middle temperature | 240 to 260 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection speed | Slow-Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 2.0 in/min |
| 4. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |