| About |
|---|
| Kingfa MAC-451PG是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa MAC-451PG的主要特性有: 阻燃/额定火焰 加工性能良好 耐冲击 典型应用领域包括: 汽车行业 涂覆应用 电气/电子应用&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Electroplating,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 19 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ASTM D790 |
| bending strength | 75.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 450 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 23.0 mm | 112 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 23.0 mm | 100 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 30 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 105 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 220 to 240 | °C | |
| Barrel middle temperature | 220 to 250 | °C | |
| Barrel front temperature | 230 to 260 | °C | |
| Processing (melt) temperature | 220 to 240 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Back pressure | 0.00 to 10.0 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |