| About |
|---|
| Kingfa PA6-G15 HSBK145 is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PA6-G15 HSBK145 are: Flame Rated Good Aesthetics Good Dimensional Stability Heat Resistant High Strength Typical application of Kingfa PA6-G15 HSBK145: Automotive&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Good Dimensional Stability,Heat Resistance, Good |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 1.2 | % | |
| MD | 0.60 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.3 | % | ISO 62 |
| Ash Content | 15 | % | ISO 3451-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 195 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 190 | MPa | ISO 2039-1 |
| Tensile modulus | 5800 | MPa | ISO 527-1-2 |
| tensile strength | 125 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2/5 |
| Bending modulus | 5000 | MPa | ISO 178 |
| bending strength | 190 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 130 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 250 to 280 | °C | |
| Processing (melt) temperature | 255 to 280 | °C | |
| Mold temperature | 40 to 90 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |