| Kingfa PA6-RG30是一种聚酰胺6（尼龙6）材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa PA6-RG30的主要特性有: 阻燃/额定火焰 Flame Retardant 高强度 耐热 Kingfa PA6-RG30的典型应用领域为:电气/电子应用&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Electrical Properties,Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD：23℃ | 0.40 | % | ASTM D955 |
| TD：23℃ | 0.90 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.60 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 220 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 215 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.90 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | 145 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.1 | % | ASTM D638 |
| Bending modulus | 8500 | MPa | ASTM D790 |
| bending strength | 210 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 220 to 240 | °C | |
| Barrel middle temperature | 240 to 260 | °C | |
| Barrel front temperature | 255 to 275 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 30 to 60 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |