| About |
|---|
| Kingfa PA6-RNG30 is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PA6-RNG30 are: Flame Rated Flame Retardant Halogen Free Typical application of Kingfa PA6-RNG30: Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low smoke,Halogen free,Low to No Fogging,Flame Characteristics |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.70 | % | |
| MD | 0.50 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.6 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 80.0 | MPa | ISO 527-2/10 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2/10 |
| Bending modulus | 5500 | MPa | ISO 178 |
| bending strength | 150 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 175 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-2 | UL 94 | |
| Glowing wire flammability index | |||
| 0.8-3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 220 to 235 | °C | |
| Barrel middle temperature | 230 to 250 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |