| About |
|---|
| Kingfa PA66-G15 is a Polyamide 66 (Nylon 66) material filled with 15% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PA66-G15 are: Flame Rated Good Aesthetics Good Dimensional Stability Heat Resistant High Strength Typical applications include: Engineering/Industrial Parts Automotive Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High elastic,low-temperature impact resistance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD：23℃ | 0.50 | % | ASTM D955 |
| TD：23℃ | 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.60 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 253 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 243 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 | |
| tensile strength | 130 | MPa | ASTM D638 |
| Bending modulus | 6100 | MPa | ASTM D790 |
| bending strength | 180 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 265 to 300 | °C | |
| Barrel front temperature | 275 to 305 | °C | |
| Processing (melt) temperature | 275 to 310 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |