| Kingfa PA66-G60 HMBK002 is a Polyamide 66 (Nylon 66) material filled with 60% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PA66-G60 HMBK002 are: Flame Rated Good Dimensional Stability Heat Resistant High Stiffness High Strength Typical application of Kingfa PA66-G60 HMBK002: Automotive&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,High Heat Resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.72 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.50 | % | |
| MD | 0.20 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.90 | % | ISO 62 |
| Ash Content | 60 | % | ISO 3451-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ISO 2039-2 | |
| Tensile modulus | 21000 | MPa | ISO 527-1-2 |
| tensile strength | 250 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/5 |
| Bending modulus | 19000 | MPa | ISO 178 |
| bending strength | 390 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 130 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 270 to 285 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 290 to 305 | °C | |
| Processing (melt) temperature | 270 to 305 | °C | |
| Mold temperature | 40 to 120 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |