| About |
|---|
| Kingfa PBT G15是一种聚丁烯对苯二甲酸酯(PBT)材料,含有的填充物为15% 玻璃纤维增强材料。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa PBT G15的主要特性有: 阻燃/额定火焰 耐热 Kingfa PBT G15的典型应用领域为:汽车行业&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD：23℃ | 0.50 | % | ASTM D955 |
| TD：23℃ | 1.1 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 95 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 215 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 208 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 | |
| tensile strength | 100 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.5 | % | ASTM D638 |
| Bending modulus | 5000 | MPa | ASTM D790 |
| bending strength | 150 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 220 to 240 | °C | |
| Barrel middle temperature | 235 to 255 | °C | |
| Barrel front temperature | 245 to 265 | °C | |
| Processing (melt) temperature | 235 to 255 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |