| Kingfa PBT JE2-R2G20是一种丙烯腈丁二烯苯乙烯 + PBT (ABS+PBT)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa PBT JE2-R2G20的主要特性有: 阻燃/额定火焰 高刚度 抗翘曲 耐化学品 热稳定剂 典型应用领域包括: 电气/电子应用 电气用具 光学/镜头 汽车行业 体育用品&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | ABS+PBT |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High elastic,Solvent resistance,Heat Stabilized,V-2 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：23℃ | 0.60 to 0.90 | % | ASTM D955 |
| MD：23℃ | 0.30 to 0.40 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 75 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 110 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 122 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.30 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 90.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.0 | % | ASTM D638 |
| Bending modulus | 7800 | MPa | ASTM D790 |
| bending strength | 145 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 82 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 245 to 265 | °C | |
| Barrel middle temperature | 240 to 260 | °C | |
| Barrel front temperature | 235 to 260 | °C | |
| Processing (melt) temperature | 235 to 260 | °C | |
| Mold temperature | 60 to 110 | °C | |
| Back pressure | 0.300 to 1.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |