| About |
|---|
| Kingfa PP-R009(f1) is a Polypropylene material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PP-R009(f1) are: Flame Rated Flame Retardant High Gloss Typical applications include: Appliances Electrical/Electronic Applications&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good liquidity,Flame Characteristics |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 to 1.06 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 23℃ | 1.4 to 1.6 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 30 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 115 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 2 mm | 750 | ℃ | IEC 60695-2-13 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 80 | ISO 2039-2 | |
| tensile strength | 30.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 50 | % | ISO 527-2/50 |
| Bending modulus | 1150 | MPa | ISO 178 |
| bending strength | 30.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 175 to 190 | °C | |
| Barrel middle temperature | 185 to 200 | °C | |
| Barrel front temperature | 190 to 205 | °C | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 0.350 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 3.2 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |