| Kingfa PVC-PMO is a Polyvinyl Chloride material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PVC-PMO are: Flame Rated Good Aesthetics Good Processability Weather Resistant Typical applications include: Appliances Electrical/Electronic Applications Engineering/Industrial Parts Wire & Cable&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Good surface appearance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：23℃ | 0.20 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 150 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 70.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 75.0 | ℃ | ASTM D1525 6 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 to 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| 1.50 mm | 5VA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, 5 seconds | 76 | ASTM D2240 | |
| Rockwell hardness | |||
| R-level | 106 | ASTM D785 | |
| tensile strength | 45.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 | % | ASTM D638 |
| Bending modulus | 2400 | MPa | ASTM D790 |
| bending strength | 65.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 70 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 140 to 160 | °C | |
| Barrel middle temperature | 150 to 170 | °C | |
| Barrel front temperature | 150 to 180 | °C | |
| Processing (melt) temperature | 180 to 210 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Injection speed | 慢to中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 2.0 in/min |
| 4. 0.079 in/min |
| 5. Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |