| About |
|---|
| Kinta NB5010G是一种聚碳酸酯（PC）产品,含有的填充物为10% 玻璃纤维增强材料。 它,在亚太地区有供货。 主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Supplier | Kinta |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.12 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 13.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 128 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 3.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+19 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | 70.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 15 | % | ASTM D638 |
| Bending modulus | 3450 | MPa | ASTM D790 |
| bending strength | 105 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 250 to 270 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |